| Hayi. | Iipropati zeResin | Ixabiso eliqhelekileyo | Iyunithi | Indlela yoVavanyo |
| 1 | Ubunzima bomxhuzulane obuthile, 23℃ | 1.05 | g/cm³ | I-ASTM D792 |
| 2 | Ukuncitshiswa kweMold, 23℃, 3.2mm, 23℃ | 0.4-0.7 | % | I-ASTM D955 |
| 3 | Izinga lokuhamba kwamanzi anyibilikayo, 220℃, 10kg | 22 | g/10min | I-ASTM D1238 |
| 4 | Amandla okuThamba xa iVula, 23℃, 50mm/min, 3.2mm | 49 | I-MPa | I-ASTM D638 |
| 5 | Ukwandiswa kokuThamba xa kuVunwa, 23℃, 50mm/min, 3.2mm | 5 | %, (Ubuncinci) | I-ASTM D638 |
| 6 | Ukwandiswa kokuThamba ngexesha lokuphumla, 23'℃, 50mm/min, 3.2mm | 10 | %, (Ubuncinci) | I-ASTM D638 |
| 7 | I-Tensile Modulus, 23℃, 50mm/min, 3.2mm | 2350 | I-MPa | I-ASTM D638 |
| 8 | Amandla okugobeka, 23℃, 15mm/min, 3.2mm | 78 | I-MPa | I-ASTM D790 |
| 9 | I-Flexural Modulus, 23℃, 15mm/min, 3.2mm | 2550 | I-MPa | I-ASTM D790 |
| 10 | Amandla e-Izod Impact, iNotched, 3.2mm, 23℃ | 220 | I-J/m | I-ASTM D256 |
| 11 | Amandla e-Izod Impact, iNotched, 3.2mm, -30℃ | 90 | I-J/m | I-ASTM D256 |
| 12 | Amandla e-Izod Impact, iNotched, 6.4mm, 23℃ | 220 | I-J/m | I-ASTM D256 |
| 13 | Amandla e-Izod Impact, iNotched, 6.4mm, -30℃ | 90 | I-J/m | I-ASTM D256 |
| 14 | Ubunzima beRockwell, i-R-Scale | 110 | / | I-ASTM D785 |
| 15 | I-HDT, i-Edgewise, i-1.82MPa, i-6.4mm, ayifakwanga | 85 | °C | I-ASTM D648 |
| 16 | I-VICAT, 50N, 50℃/h | 92 | °C | I-ASTM D1525 |
| 17 | Umbane we-RTI | 95 | °C | UL 746B |
| 18 | I-RTI Mechanical enempembelelo | 95 | °C | UL 746B |
| 19 | I-RTI Mechanical ngaphandle kweMpembelelo | 95 | °C | UL 746B |
| 20 | Ukutsha, 1.5mm | HB | / | UL 94 |
| 21 | Ukutsha, 3.0mm | HB | / | UL 94 |